Complete technical data sheet with print conditions, material properties, and performance specifications.
| Manufacturer | Polymaker | |
| Product Name | PC-ABS | |
| Filament Type | PC-ABS | |
| Finish | Blend |
| Nozzle Temperature | 260-280°C | |
| Bed Temperature | 90-110°C | |
| Print Speed | 30-60mm/s | |
| Cooling Fan | Off | |
| Retraction Distance | 3-6mm | |
| Retraction Speed | 40-60mm/s | |
| Build Surface Materials | Glass PEI |
| Diameter | 1.75-2.85mm | |
| Density | 1.1g/cm³ | ISO 1183 |
| Glass Transition Temperature | 108°C | DSC, 10°C/min |
| Vicat Softening Temperature | 112°C | ISO 306 |
| Heat Deflection Temperature @ 1.8MPa | 93°C | ISO 75 |
| Heat Deflection Temperature @ 0.45MPa | 105°C | ISO 75 |
| Melt Index | 10g/10 min | 260°C, 2.16kg |
| Young's Modulus (X-Y) | 2152MPa | ISO 527 |
| Young's Modulus (Z) | 1821MPa | ISO 527 |
| Tensile Strength (X-Y) | 42.29MPa | ISO 527 |
| Tensile Strength (Z) | 30.92MPa | ISO 527 |
| Elongation at Break (X-Y) | 2.6% | ISO 527 |
| Elongation at Break (Z) | 2.23% | ISO 527 |
| Flexural Modulus (X-Y) | 2068MPa | ISO 178 |
| Flexural Strength (X-Y) | 69.29MPa | ISO 178 |
| Charpy Impact Strength (X-Y) | 27.8kJ/m² | ISO 179 |
| Effect of Weak Acids | Good | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/polycarbonate/polymaker-pc-abs |
| Effect of Weak Alkalis | Fair | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/polycarbonate/polymaker-pc-abs |
| Effect of Oils & Grease | Good | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/polycarbonate/polymaker-pc-abs |
| Effect of Strong Acids | Poor | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/polycarbonate/polymaker-pc-abs |
| Effect of Strong Alkalis | Poor | https://wiki.polymaker.com/polymaker-products/more-about-our-products/documents/technical-data-sheets/polycarbonate/polymaker-pc-abs |